Lapox® ARBZ-10 & Lapox® ARBZ-11 ( Benzoaxazine Resin)
ATUL LTD
Lapox® ARBZ-10 is bisphenol-F based difunctional and halogen free benzoxazine thermoset resin. This can be homopolymerised or co-cured with epoxy, phenol or suitable catalyst resulting in polymers with excellent thermal and mechanical properties. Res...
Lapox® ARBZ-10 is bisphenol-F based difunctional and halogen free benzoxazine thermoset resin. This can be homopolymerised or co-cured with epoxy, phenol or suitable catalyst resulting in polymers with excellent thermal and mechanical properties. Resin ARBZ-10 is suitable for high performance applications due to very low water absorption and curing shrinkage along with high glass transition temperature. Advantages Good moisture resistant Low smoke toxicity Excellent chemical & thermal resistant High glass transition temperature Excellent electrical properties Low shrinkage Low coefficient of thermal expansion Good flammability resistant UL94 V1 Lapox® ARBZ-11 is bisphenol-A based difunctional and halogen free benzoxazine thermoset resin. It can be homopolymerised or co-cured with epoxy, phenol or suitable catalyst resulting in polymers with excellent thermal and mech. properties.Suitable for high performance applications due to low water absorption and curing shrinkage & high Tg.
Brand: LAPOX
Specification:ARBZ-10 Appearance -- Visual Yellowish solid Melt viscosity at 100°C mPas ASTM D 4287 1000 - 7000 Gel time at 220°C seconds DIN 16945 200 - 450 Softening point °C ATUL 60 - 80 Glass transition temp. (Tg)* °C DSC 145 - 155 **Cure schedule: 3hrs at 170°C + 2hrs at 180°C + 4hrs at 200°C ARBZ-11 Appearance -- Visual Yellowish solid Viscosity at 125°C mPas ASTM D 4287 50 - 500 Gel time at 220°C seconds. DIN 16945 250 - 550 Softening point °C ATUL 60 - 80 Glass transition temp. (Tg)* °C DSC 160 - 170 **Cure schedule: 2hours at 180°C + 2hours at 200°C
Download